The aim of this work is evaluation of corrosion behavior of SS 304 coated through TIG process. In this work, Ti tube cored with graphite powder was applied. Experimental processes were shown that the optimum parameters for coating procedure are voltage of 15V, current density of 120A and the speed of 2.1mm/s. Investigations on corrosion resistance of coating are shown that not only this composite coating can improve the tribological behavior of this type of stainless steel, but also there is an improvement in its deteriorative property. Moreover, it is observed that mass reduction in coating is 5 times lower than the base metal.