The microstructure and solidification behavior of nickel based GTD222 superalloy at different cooling rates are studied. The solidification of the GTD222 superalloy proceeds as follows: L→L+γ, L→L+γ+MC, L→L+(γ/γ ′)-Eutectic and L→η phase. The temperature of liquidus of GTD222 superalloy is 1360 °C while the solidus is slightly lower at 1310 °C, which due to the alloying elements redistribution. It was found that the dendrite arm spacing of the alloy decreased with the increase of cooling rate (From 200 μm at 2.5 K/min to 100 μm at 20 K/min).