This paper presents the results of investigations of the effects of hot deformation parameters in compression investigation on the austenite grain size in HSLA steel (0.16% C, 0.037% Nb, 0.004% Ti, 0.0098% N). The axisymmetric compression investigations were performed on cylindrical investigation specimens of d=1.2 using the Gleeble 3800 simulator. The strain rate=1s-1÷15.9s-1 and strain degree ε=1.2. Before deformation, the research specimens were austenitized at TA = 1100 ÷ 1250 °C. Metallographic observations of the primary austenite grains were conducted with an optical microscope, while the structure of dynamically recrystallized austenite, inherited by martensite, was examined by EBSD technique using a scanning electron microscope. Based on the analysis of investigation results, it was found that the size of dynamically recrystallized austenite grains in HSLA steel were clearly affected by hot compression parameters. In contrast, no significant impact of austenitising temperature on their size was found.