DNA damage repair lies at the core of all cells’ survival strategy, including cancerous. Therefore, targeting such repair mechanisms forms the major goal of cancer therapeutics. The mechanism of DNA repair has been tousled with the discovery of multiple kinases. Recent studies on Tousled like Kinases have brought significant clarity on the effectors of these kinases which stands to regulate DSB repair. In addition to their well-established role in the DDR and cell cycle checkpoint mediation after DNA damage or inhibitors of replication, their suspected involvement in the actual DSB repair process has more recently been strengthened by the important finding that TLK1 phosphorylates RAD54 and regulates some of its activities and localization in the cell. Earlier findings of its regulation of RAD9 during checkpoint deactivation as well as defined steps during NHEJ ends processing were earlier hints of its important involvement broadly in DSB repair. All this has opened up new avenues to target cancer cells in combination therapy with genotoxins and TLK inhibitors.

In this study, unlike conventional methods for producing vanadium (3.5+) electrolyte by VOSO4 and V2O5, a batch-type hydrothermal reactor was used to produce a vanadium (3.5+) electrolyte for vanadium redox flow batteries through a reduction reaction. The starting material, V2O5, was mixed with different concentrations of citric acid (0.8M, 1.2M, 1.6M, 2.0M) as reducing agent and stirred using a hot plate at 90°C for 60 minutes to achieve complete dispersion in the solution. The resulting solution was then subjected to a hydrothermal reduction reaction in a furnace at 150°C for 24 hours to produce vanadium (3.5+). The mixed state of the produced vanadium (3+) and vanadium (4+) was confirmed using UV-vis spectroscopy. Electrochemical properties were investigated through CV analysis, confirming that the optimal concentration was 1.6M. Charge and discharge experiments were conducted to compare the current efficiency, energy efficiency, and voltage efficiency of the electrolyte prepared by the hydrothermal reduction process and the electrolyte prepared by VOSO4. As a result, the electrolyte produced through the hydrothermal reduction process showed improved performance in all efficiencies. The results shows that vanadium (3.5+) electrolyte could be easily produced through a reaction process using citric acid.